Role of the Al chemical environment in the formation of silver species and its CO oxidation activity
  • 点击次数:
  • 论文类型:期刊论文
  • 发表时间:2015-01-01
  • 发表刊物:JOURNAL OF CATALYSIS
  • 收录刊物:SCIE、EI
  • 文献类型:J
  • 卷号:321
  • 页面范围:113-122
  • ISSN号:0021-9517
  • 关键字:Ag species; Al chemical environment; Al-SBA-15; CO oxidation
  • 摘要:An understanding of active species-metal oxide support interaction is a necessary prerequisite for finely tuning the catalytic performance of Ag-based catalysts. To shed light on the interrelationship between Ag structures and acidic sites of acidic supports, a series of Ag/Al-SBA-15 catalysts with different Si/Al ratios were prepared using in situ "pH-adjusting" method and tested for catalytic CO oxidation. Of all the catalysts employed, the one with a Si/AI molar ratio of 200 (Ag/MAS 200) outperformed other catalysts in terms of activity and durability. Al-27 NMR and H-1 NMR results showed that the octahedrally coordinated extra-framework Al connected to the framework via oxygen atoms suppressed the formation of H-bonded SiOH groups, resulting in the formation of highly dispersed Ag nanoparticles with high catalytic activity. In the meantime, the presence of Ag2O particles formed over the framework Al with bridging hydroxyl groups considerably deteriorated the catalytic performance. However, the Ag/MAS 200 catalyst exhibited a striking feature: that is, the bulk Ag2O species are easily reduced by CO at room temperature, leading to "in situ formation" of metallic Ag particles during CO oxidation even in the presence of high concentration of O-2. This unique property caused the induction period (ca. 270 min) and gradually enhanced the catalytic activity, eventually reaching a high and steady-state CO conversion (85%). (c) 2014 Elsevier Inc. All rights reserved.

上一条: Highly dispersed Fe2O3 on carbon nanotubes for low-temperature selective catalytic reduction of NO with NH3

下一条: Structure sensitivity of mesoporous iron-cerium oxides for selective catalytic reduction of NOx with NH3