发表刊物：CARBON

收录刊物：SCIE

卷号：139

页面范围：716-724

ISSN号：0008-6223

摘要：Nitrogen-doped carbon materials hold great potential for high-performance lithium storage. However, the excess defects introduced by dominated nitrogen doping methods may lead to a thickened solid electrolyte interphase (SEI), resulting in a higher Li+ diffusion resistance and inferior rate performance. Herein, composite carbon nanofibers (CNEs) with tuned microstructure and relatively high nitrogen content were fabricated by co-electrospinning the mixture of nitrogen-rich pitch, a soft carbon precursor, with polyacrylonitrile (PAN) in controlled mass ratio. The result shows that the SEI formed on the composite CNEs with less surface defects is much thinner yet tighter than that formed on the PAN-based CNEs. As such, the composite CNEs present a double capacity retention of 37.3% to that of the PAN-based CNEs at 10 Ag-1. More importantly, the cycle retention of the composite CNEs anode is 88.0% after 1000 cycles at 2 Ag-1, much higher than that of PAN-based CNEs (61.5%). It is believed that the improved rate and cycle performance are due to the superior structure and chemical composition of the SEI, which can be attributed to the modified microstructure by addition of nitrogen-rich pitch to a great extent. (C) 2018 Published by Elsevier Ltd.