Date of Publication:2021-01-29

Journal:ACTA MATERIALIA

Volume:131

Page Number:169-186

ISSN No.:1359-6454

Key Words:K403 Ni based superalloy; Thermal exposure; Carbide; Topologically close-packed phase; HAADF-STEM; EELS

Abstract:The microstructure evolution of the K403 Ni-based superalloy as a function of thermal exposure temperature and time was investigated using correlative characterization, including a combination of scanning electron microscopy, electron backscatter diffraction, transmission electron microscopy, high angle angular dark-field scanning transmission electron microscopy imaging and electron energy loss spectroscopy. The as-cast microstructure of the K403 alloy shows a typical dendritic structure and consists of a gamma solid solution, gamma' phase, (gamma + gamma') eutectic phase and a metal carbide (MC) phase. The solutes of Ni and Ti are enriched in the gamma solid solution, while, the solutes of Cr and Co are enriched in the gamma' phase. The morphology of the y' phase is nearly cubic. After thermal exposure at 800 degrees C or 950 degrees C for up to 200 h, the typical dendritic structure and a similar solute segregation behavior were still observed. However, the MC carbides were partially decomposed and further transformed to the M6C phase and M23C6 phase. Furthermore, the size of y' was increased from 302.88 +/- 20.49 nm to 374.75 +/- 29.76 nm (800 degrees C, 50 h) and 751.73 +/- 123.14 nm (950 degrees C, 50 h), respectively. The morphology of y' was changed from cubic to triangular or round. Clearly, there is a significant coarsening of y' during thermal exposure. A topologically close-packed (TCP) a phase was observed after thermal exposure at 800 degrees C for 100 h or 950 C for 50 h. More interestingly, an in-situ phase transformation of the a phase to other TCP phase (i.e. P phase) was also observed after thermal exposure at 950 degrees C for 50 h. The formation and transformation of carbide (i.e. M6C phase, M23C6 phase) and TCP phases (i.e. a phase, P phase) is proposed to be a diffusion-controlled process and can be attributed to the solute diffusion during thermal exposure. The present investigation provides a better understanding on the high temperature performance of the K403 Ni-based superalloy, which is essential to predict the failure and thereby enhance the reliability and service life of the K403 Ni-based superalloy. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.