点击次数：

发布时间：2019-03-09

论文类型：期刊论文

发表时间：2015-02-04

发表刊物：ACS APPLIED MATERIALS & INTERFACES

收录刊物：ESI高被引论文、Scopus、PubMed、EI、SCIE

卷号：7

期号：4

页面范围：2444-2451

ISSN号：1944-8244

关键字：tin dioxide; graphene; polyaniline; phytic acid; Li-ion batteries

摘要：Dually fixed SnO2 nanoparticles (DF-SnO2 NPs) on graphene nanosheets by a polyaniline (Pani) coating was successfully fabricated via two facile wet chemistry processes, including anchoring SnO2 NPs onto graphene nanosheets via reducing graphene oxide by Sn2+ ion, followed by in situ surface sealing with the Pani coating. Such a configuration is very appealing anode materials in LIBs due to several structural merits: (1) it prevents the aggregation of SnO2 NPs, (2) accommodates the structural expanding of SnO2 NPs during lithiation, (3) ensures the stable as-formed solid electrolyte interface films, and (4) effectively enhances the electronic conductivity of the overall electrode. Therefore, the final DF-SnO2 anode exhibits stable cycle performance, such as a high capacity retention of over 90% for 400 cycles at a current density of 200 mA g(-1) and a long cycle life up to 700 times at a higher current density of 1000 mA g(-1).