Indexed by: Journal Article

Date of Publication: 2010-08-01

Journal: 16th International Symposium on Metastable, Amorphous and Nanostructured Materials

Included Journals: Scopus、CPCI-S、EI、SCIE

Volume: 504

Issue: SUPPL. 1

Page Number: S2-S5

ISSN: 0925-8388

Key Words: Bulk metallic glass; Mechanical property; Zr-based alloys; Compressive strain

Abstract: The thermal stability, melting behavior, and glass-forming ability of Zr(70)Al(8)Cu(22-x)Ni(x) (x = 3-19 at.%) metallic glasses were investigated. Fully glassy sample with largest critical diameter of 10 mm was obtained for alloy with x = 8.5 in the alloy series, which corresponds to a deep eutectic, largest supercooled liquid region, and largest gamma value. Room temperature compression test revealed that the monolithic Zr(70)Al(8)Cu(13.5)Ni(8.5) bulk metallic glass exhibits a high yield strength of 1570 MPa, a Young's modulus of 80 GPa, and a super large plastic strain more than 70%. (C) 2010 Elsevier B.V. All rights reserved.