发表刊物：16th International Symposium on Metastable, Amorphous and Nanostructured Materials

收录刊物：SCIE、EI、CPCI-S、Scopus

卷号：504

期号：SUPPL. 1

页面范围：S2-S5

ISSN号：0925-8388

关键字：Bulk metallic glass; Mechanical property; Zr-based alloys; Compressive strain

摘要：The thermal stability, melting behavior, and glass-forming ability of Zr(70)Al(8)Cu(22-x)Ni(x) (x = 3-19 at.%) metallic glasses were investigated. Fully glassy sample with largest critical diameter of 10 mm was obtained for alloy with x = 8.5 in the alloy series, which corresponds to a deep eutectic, largest supercooled liquid region, and largest gamma value. Room temperature compression test revealed that the monolithic Zr(70)Al(8)Cu(13.5)Ni(8.5) bulk metallic glass exhibits a high yield strength of 1570 MPa, a Young's modulus of 80 GPa, and a super large plastic strain more than 70%. (C) 2010 Elsevier B.V. All rights reserved.