发表刊物：RARE METALS

收录刊物：SCIE、EI、CSCD

卷号：32

期号：4

页面范围：354-358

ISSN号：1001-0521

关键字：Ti-Cr-V alloys; Cluster; Hydrogen storage properties; Copper mould suction casting

摘要：The microstructure and hydrogen storage properties of low V content (Ti0.46Cr0.54)(100-x) V (x) (x = 2.5-7.1, at%) and (Ti (y) Cr1-y )(95)V-5 (y = 0.38-0.54) alloys were investigated. These alloys were prepared by arc melting and copper mould suction casting. The structures of as-cast (Ti0.46Cr0.54)(100-x) V (x) (x = 2.5, 5.0, and 7.1) alloy ingots evolve with V contents from pure Laves- (x = 2.5) to dual-phase TiCr2-BCC structures (5.0 and 7.1), whereas the suction-cast (Ti0.46Cr0.54)(100-x) V (x) (x = 2.5, 5.0, and 7.1) alloys only contain single BCC phase. The suction-cast alloy rod (Ti0.46Cr0.54)(95)V-5, containing only 5.0 at% V is shown to possess the optimum hydrogen absorption capacity, with the maximum hydrogen content of 3.14 wt%. Furthermore, the hydrogen storage properties of the suction-cast low V alloys (Ti (y) Cr1-y )(95)V-5 (y = 0.38-0.54) are sensitive to Ti/Cr ratios and only those alloys with Ti/Cr ratios close to the CN14 cluster [Ti7Cr8] have good hydrogen storage properties.