发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

收录刊物：SCIE、EI

卷号：550

页面范围：423-428

ISSN号：0921-5093

关键字：Aluminum; Steel; Welding; Post-weld heat treatment; Microstructure; Mechanical properties

摘要：Lap joining of 5A02 aluminum alloy to 304 stainless steel sheets was conducted by gas tungsten arc welding with Zn-15%Al flux-cored filler wire, and the effects of the temperature and duration time during post-weld heat treatment on the microstructure and mechanical properties of the resultant joints were investigated. The experimental results show that the concentration and size of the Zn-rich phases in the weld, especially along the weld/steel interface, changed with different temperature and duration time, and consequently affected the joint strength. The fine Zn-rich phases uniformly distributed in the weld could enhance the joint strength; however, the coarse Zn-rich phases along the interfacial layer would degrade the bonding strength of the interfacial layer. The fractured surfaces of the specimens after tensile testing were also examined. (C) 2012 Elsevier B.V. All rights reserved.