点击次数：

论文类型：期刊论文

发表时间：2010-05-01

发表刊物：INTERMETALLICS

收录刊物：SCIE、EI

卷号：18

期号：5

页面范围：791-795

ISSN号：0966-9795

关键字：Alloy design; Glasses; metallic; Mechanical properties at ambient temperature; Rapid solidification processing; Corrosion behavior

摘要：The formation of Ni-based B-Fe-Ni-Si-Ta bulk metallic glasses is explored in this work. The alloy compositions are determined by using a combination of the cluster line approach, the minor alloying strategy and the substitutions of similar elements. The basic B-Ni-Si ternary compositions are first determined by the intersection points of different cluster lines, B-Ni cluster to Si and Ni-Si cluster to B, and then are minor-alloyed with 4 at.% Ta. Finally Fe is added to partially substitute for Ni to further improve the glass-forming abilities. Bulk metallic glasses with diameters of 3 mm are formed at compositions [Br-17.7(Ni1-xFex)(70.5)](Si7.8Ta4), x=0.35-0.45, which also exhibit good mechanical and corrosion-resistant properties. Furthermore, these compositions can be expressed using our cluster-plus-glue-atom model as [B-2(Ni,Fe)(8)](1)(Si,Ta)(1.33). BMGs with compositions satisfying [B-2(Ni,Fe)(8)](Si, Ta)(1) are also obtained. (C) 2009 Published by Elsevier Ltd.