发表刊物：ACS CATALYSIS

收录刊物：SCIE、EI

卷号：7

期号：3

页面范围：1868-1874

ISSN号：2155-5435

关键字：bismuth vanadate; water splitting; photoanode; passivation; ferrihydrite

摘要：In spite of great progress in the surface modification of semiconductor photoelectrodes, the role of the metal oxide cocatalyst on photoelectrochemical (PEC) performance is still not well understood. In this study, ferrihydrite (Fh) as a novel cocatalyst was decorated on a wormlike nanoporous BiVO4 photoanode. A surface kinetics study of Fh/BiVO4 by intensity-modulated photocurrent spectroscopy (IMPS) evidences the primary role of Fh on PEC performance enhancement, varying with the loading of Fh. It was found that dispersed Fh le nanoparticles accelerate hole transfer for water oxidation, but the resulting photoanode suffers from poor stability. The thick layers of Fh address the stability of the electrode by suppressing surface charge recombination but result in reduced hole transfer rates. Modification of a BiVO4 film with optimally thick layers of discrete nanoflakes effectively reduces charge recombination without compromising stability, leading to a high AM 1.5 G photocurrent of 4.78 mA/cm(2) at 1.23 V versus the reversible hydrogen electrode and an applied bias photon to current efficiency of 1.81% at 0.61 V. These values are comparable to the best results reported for undoped BiVO4.