A new type Ni-MOF catalyst with high stability for selective catalytic reduction of NOx with NH3
点击次数：
论文类型：期刊论文
发表时间：2018-08-01
发表刊物：CATALYSIS COMMUNICATIONS
收录刊物：SCIE
卷号：114
页面范围：104-108
ISSN号：1566-7367
关键字：Environmental catalysis; Ni-MOF catalyst; Porous materials; Selective catalytic reduction; Active temperature
摘要：A crystalline porous Ni-MOF catalyst was fabricated successfully through hydrothermal method and shown to exhibit excellent catalytic performance for NH3-SCR. This prepared Ni-MOF showed better thermal stability than other reported Cu-BTC or MIL-100(Fe) SCR catalyst material. It could keep a satisfactory stable crystalline structure when the reaction temperature reached up to 440 degrees C. Moreover, it was found that the catalytic activity of Ni-MOF was significantly improved after preheat treatment in N-2 atmosphere. The Ni-MOF catalyst activated at 220 degrees C achieved more than 92% NO conversion efficiency with a large operating-temperature window from 275 to 440 degrees C.
上一条：Highly oriented SnS2/RGO/Ag heterostructures for boosting photoeletrochemical and photocatalytic performances via schottky and RGO-n dual-heterojunctions interfacial effects
下一条：Polydopamine-assisted decoration of TiO2 nanotube arrays with enzyme to construct a novel photoelectrochemical sensing platform