发表时间：2017-11-24

发表刊物：NANOTECHNOLOGY

收录刊物：SCIE、EI、PubMed

卷号：28

期号：47

页面范围：475401

ISSN号：0957-4484

关键字：N-doping; MnO2 nanosheets; combined chemisorption; lithium-sulfur batteries

摘要：In this work, nitrogen-doped hollow porous carbon nanospheres coated with MnO2 nanosheets (NHPC@MnO2) were prepared as a novel sulfur host for the cathode of lithium-sulfur battery. N-doping of carbon and deposition of the inherently polar MnO2 promote chemical binding of the host with sulfur and its reduction products, known as polysulfides. Meanwhile, proper N-doping can improve the electron conductivity of carbon, and the nanosheet structure may help to guarantee facile electron-and lithium-ion transport through MnO2. Attributed to these advantages, the NHPC@MnO2/S cathode with a high sulfur content (70 wt% and 2.6 mg cm(-2)) exhibited an excellent cycle stability: its capacity retention was 93% within 100 cycles at 0.5 C. It also displayed a good rate capability: discharge capacities being similar to 1130 mAh g(-1) at 0.2 C, similar to 1000 mAh g(-1) at 0.5 C, similar to 820 mAh g(-1) at 1 C, and similar to 630 mAh g(-1) at 2 C. Our work demonstrates the synergistic effect of MnO2 nanostructure and N-doped carbon nanospheres for enhanced performance of lithium-sulfur battery cathodes.