A study of structure and properties of Ti-doped DLC film by reactive magnetron sputtering with ion implantation
点击次数：
论文类型：期刊论文
发表时间：2012-01-15
发表刊物：APPLIED SURFACE SCIENCE
收录刊物：SCIE、EI
卷号：258
期号：7
页面范围：3045-3050
ISSN号：0169-4332
关键字：Ti doping; DLC; Ion implantation; Adhesion; Hydrophobic property
摘要：Ti-doped diamond- like carbon (DLC) films were prepared on Ti alloys by reactive magnetron sputtering combined with PSII technology. The structure and properties of unmodified and Ti-doped DLC films were analyzed in a systematic way by different testing, such as TEM, XPS, frictional wear testing, contact angle measurement and so on. The results showed that Ti-doped DLC was a typical a-C:H film containing TiC nanometer grains, whose mechanical properties were obviously improved, such as hardness, wear resistance and cohesive strength, still kept good wear resistance at the ambient temperature of 450 degrees C, and held a rather large mean water contact angle of 104.2 +/- 1 degrees. (C) 2011 Elsevier B. V. All rights reserved.