Corrosion behavior of as-cast Mg-5Sn based alloys with In additions in 3.5 wt% NaCl solution
点击次数：
论文类型：期刊论文
发表时间：2020-03-01
发表刊物：CORROSION SCIENCE
收录刊物：EI、SCIE
卷号：164
ISSN号：0010-938X
关键字：Magnesium alloy; In; Electrochemical test; Corrosion behavior
摘要：The corrosion behavior of as-cast Mg-5Sn-xIn (x = 0, 1, 2, 3, 4, all in wt%) alloys in 3.5 wt% NaCl solution was investigated using weight loss, hydrogen evolution and electrochemical test. The results showed that the microstructures of all alloys consisted of typical coarse dendrites without the presence of any In-rich phase. The corrosion resistance of Mg-5Sn-xIn alloys was enhanced monotonously with increasing In content up to 3 wt%. The electrochemical measurements revealed that such improvements could be mainly attributed to the retardation of cathodic reaction, decreasing the rate of hydrogen evolution.