点击次数：

论文类型：期刊论文

发表时间：2017-07-01

发表刊物：MATERIALS TESTING

收录刊物：SCIE、EI

卷号：59

期号：7-8

页面范围：635-641

ISSN号：0025-5300

关键字：Welding parameters; residual stresses; welded specimens; crack opening displacement; digital image correlation

摘要：To investigate the effect of weld induced residual stresses on the crack performance, standard compact tension specimens were cut into two pieces, then joined to form welded specimens under various welding conditions. The crack opening displacement was measured by digital image correlation technique. It is found that specimens welded in the opposite direction show smaller crack opening displacement than those welded in the same direction. The crack opening displacement decreased as the distance from the crack tip to the center of weld line was increased from 8 mm to 30 mm. The crack opening displacement of the specimens with 30-minute time interval was lower than that of the specimens without interval, regardless of welding directions.