发表时间：2020-02-01

发表刊物：IONICS

收录刊物：EI、SCIE

卷号：26

期号：2

页面范围：1003-1009

ISSN号：0947-7047

关键字：PTFE; (PMo12O40)(X)-(PO-OH)(Y); High-temperature; PEMFC; Proton conductivity

摘要：A novel high-temperature proton exchange membrane (PEM) (PTFE/(PMo12O40)(X)-(PO-OH)(Y) composite membranes) was prepared by impregnating mixed acid into the porous PTFE membrane. The porous PTFE membrane serves as the support structure of the membrane, and (PMo12O40)(X)-(PO-OH)(Y) sol is used as the proton conductor. The solid poly acid (PMo12O40)(X)-(PO-OH)(Y) exhibits a proton conductivity of 0.025 S cm(-1) at 180 degrees C, and the PTFE/(PMo12O40)(X)-(PO-OH)(Y) membrane presents a good proton conductivity (0.02 S cm(-1)) when the relative humidity is below 0.5% and temperature is 180 degrees C. Besides, the PTFE/(PMo12O40)(X)-(PO-OH)(Y) membrane performs moderate property as tested in hydrogen fuel cells. SEM and EDX reveal that the structure of (PMo12O40)(X)-(PO-OH)(Y) gel is uniformly distributed in the pores of PTFE, which enhanced the proton conductivity of the composite membranes.