发表刊物：INTERNATIONAL JOURNAL OF HYDROGEN ENERGY

收录刊物：SCIE、EI

卷号：36

期号：16

页面范围：10022-10026

ISSN号：0360-3199

关键字：PTFE; Quaternary DABCO polysulfone; Composite membrane; Alkaline anion exchange membrane; Fuel cell

摘要：The quaternary 1,4-diazabicyclo-[2.2.2]-octane (DABCO) polysulfone (QDPSU) was synthesised. A thin (30 mu m) composite membrane based on polytetrafluoroethylene (PTFE) and QDPSU was obtained by impregnation method of QDPSU solution in PTFE support. SEM images revealed a dense and homogenous structure of PTFE-QDPSU membrane. The PTFE-QDPSU composite membrane showed good mechanical strength (a 32 MPa maximum load), and a water uptake of 61 +/- 3% and a 17 +/- 2% swelling degree. An ionic conductivity of 0.051 S cm(-1) was achieved at 50 degrees C and 100% RH. Preliminary data of a single MEA gave power outputs of 146 and 103 mW cm(-2) with oxygen and air respectively. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.