Effect of Welding Speed in High Speed Laser-TIG Welding of Magnesium Alloy
点击次数:
论文类型:期刊论文
发表时间:2012-01-01
发表刊物:MATERIALS AND MANUFACTURING PROCESSES
收录刊物:SCIE、Scopus
卷号:27
期号:12
页面范围:1424-1428
ISSN号:1042-6914
关键字:Hardness; Liner-energy; Microstructures; Speed; Tensile-strength; Welding
摘要:In order to investigate the effect of welding speed on microstructures and mechanical properties in high speed welding, low power laser-tungsten inert gas (laser-TIG) hybrid welding process is proposed on AZ61 magnesium alloy. Defect-free welds are produced by employing welding speed ranging from 2,000 mm/min to 6,000 mm/min. It is found that welding speed has a significant influence on microstructures and mechanical properties of the joints. Results indicate that with rapid increasing of welding speed, both the liner energy and average grain size decrease on the premise that fully-penetrated joints with no macroscopic porosities or cracks are obtained. The microhardness in the weld fusion zone increases with the welding speed. It is also found that the tensile strength decreases after an increase with the increase in welding speed. The fracture mode changes from mixture fracture of ductile and brittle to typical intergranular fracture feature.
上一条:The effect of alloying elements on shear strength of lap joint of AZ31B magnesium alloy to Q235 steel by hybrid laser-TIG welding technique
下一条:Tensile Mechanical Properties and Strengthening Mechanism of Hybrid Carbon Nanotube and Silicon Carbide Nanoparticle-Reinforced Magnesium Alloy Composites