发表刊物：MATERIALS CHARACTERIZATION

收录刊物：SCIE

卷号：59

期号：4

页面范围：479-483

ISSN号：1044-5803

关键字：Contact Reaction Brazing (CRB); Mg alloy; Al alloy; microstructure; property

摘要：This work focuses on the microstructure and properties of Mg alloy and Al alloy brazed joints prepared with different thickness of Zn filler metal, ranging from 0 to 30 mu m. Mg alloy and Al alloy can be bonded successfully by Contact Reaction Brazing (CRB) with and without Zn filler metal in a traditional air furnace. The addition of the Zn filler metal can significantly improve the tensile strength. The reaction layer became thin with the use of thinner Zn filler-metal layers, while the thinner reaction layer brought about higher shear strength. The best results were associated with a bonding temperature of 360 degrees C and the use of a 3 mu m Zn filler metal to produce bonded joints in times ranging from 10 to 30 min. (c) 2007 Elsevier Inc. All rights reserved.