点击次数：

论文类型：会议论文

发表时间：2014-07-04

收录刊物：EI、Scopus

卷号：816

页面范围：3-8

摘要：Carbon fiber is mainly distributed in the shape of short fibers and unidirectional fibers as the reinforcing phase in metal matrix composites, and it is seldom studied as woven-cloth shaped to reinforce the matrix. In this paper, the pretreatment and the surface metallization of the woven carbon fiber were studied. Besides, the casting experiment without external pressure was carried out under the application of magnetic field. The result shows that when burning about 45mins at 500   in the atmospheric environment, the pretreatment can achieve the best result according to differential thermal analysis and weight-time variation curve. Meanwhile the surface wettability between the carbon fiber and the matrix is greatly improved after the surface treatment and at the same time the reaction between the carbon fiber and molten aluminium alloy matrix is necessarily avoided, and it can consequently achieve an excellent bonding between the woven carbon fiber and aluminium alloy matrix. The application of magnetic field also provides magnetic force to promote the penetration of the molten matrix into the carbon fiber bundles. ? (2015) Trans Tech Publications, Switzerland.