点击次数：

论文类型：会议论文

发表时间：2013-09-22

收录刊物：EI、Scopus

卷号：789

页面范围：48-53

摘要：A bulk casting ingot (?70    150mm) of CoCrFeNiTi0.5 high entropy alloy was prepared by vacuum medium frequency induction melting. The samples from the ingot were aged for 12h in the temperature range of 900-1100  C and then quenched in water to investigate the effect of aging temperature on the microstructure and hardness of CoCrFeNiTi0.5 alloy. The crystalline structure of as-cast CoCrFeNiTi0.5 alloy consisted of the principal face-centered cubic (FCC) dendrite phase plus (Ni, Ti)-rich R phase, (Fe, Cr)-rich    phase, (Co, Ti)-rich Laves phase within the inter-dendrite area. The dendrite contained approximately equivalent amount of Co, Cr, Fe, Ni and a smaller amount of Ti element. After aging treatment in the temperature range of 900-1000  C, the (Co, Ti)-rich phase disappeared while the amount of (Ni, Ti)-rich phase and (Fe, Cr)-rich phase increased. But the volume fraction of FCC dendrite phase increased and the intermetallic phases decreased after aging at 1100  C. The micro-hardness and the macro-hardness of the as-cast CoCrFeNiTi0.5 alloy were HV616.8 and HRC52, respectively. After heat treatment at 1000  C, the micro-hardness and macro-hardness decreased from HV616.8 to HV386.8 and from HRC52 to HRC42.7, respectively. ? (2014) Trans Tech Publications, Switzerland.