点击次数：

论文类型：期刊论文

发表时间：2013-03-01

发表刊物：METALS AND MATERIALS INTERNATIONAL

收录刊物：SCIE

卷号：19

期号：2

页面范围：367-370

ISSN号：1598-9623

关键字：alloys; cast; microstructure; solidification; scanning electron microscopy

摘要：The improved halide salt route has been employed to produce Al-3B master alloys with different microstructures. The micro-structural features of AlB2 particles exhibited different impacts on the grain refining response of Al-7Si alloy, evolving with the holding time after inoculation. Large blocky AlB2 particles suffer from an intense fading effect while strip-like particles are not effective enough at the 0.005 wt% B addition level. Among the various Al-3B master alloys, sample 1 containing fine, blocky AlB2 particles was revealed to be the most efficient in refining Al-7Si alloy. With inoculation of only 0.005%B of such alloy, the final grain size of Al-7Si alloy can reach 238 mu m. Its grain refining efficiency was more or less retained for holding times up to 60 min.