点击次数：

论文类型：期刊论文

发表时间：2009-06-01

发表刊物：MATERIALS CHARACTERIZATION

收录刊物：SCIE、EI

卷号：60

期号：6

页面范围：482-486

ISSN号：1044-5803

关键字：Magnesium alloy; Sub-rapid solidification; Microstructure; Microdistribution

摘要：AZ61 magnesium alloy foils of 0.5-3.0 mm thick were successfully produced by using sub-rapid solidification technique. Microstructures of conventionally solidified (CS) and sub-rapidly solidified (sub-RS) alloys were examined by optical microscope (OM) and scanning electron microscope (SEM). The results showed that the cellular grain of 1.8-13.5 mu m can be obtained during sub-rapid solidification process. Phase compositions and microdistribution of the alloying elements in the foils were analyzed by X-ray diffraction (XRD) and electron probe microanalyzer (EPMA), respectively. The eutectic transformation L ->alpha-Mg+beta-Mg(17)Al(12) and microsegregation in conventionally solidified AZ61 alloy were remarkably suppressed in sub-rapid solidification process. As a consequence, the alloying elements Al, Zn, Mn showed much higher solid solubility and the sub-rapid solidification microstructures dominantly consisted of supersaturated alpha-Mg solid solution. Meanwhile, the beta-Mg(17)Al(12) phases located in the alpha-Mg grain boundaries are largely decreased due to high solidification cooling rate. (C) 2008 Elsevier Inc. All rights reserved.