Semi-solid slurry of AZ91 magnesium alloy prepared by electromagnetic stirring near liquidus temperature

点击次数:

论文类型:期刊论文

发表时间:2007-08-01

发表刊物:CHINA FOUNDRY

收录刊物:SCIE

卷号:4

期号:3

页面范围:186-189

ISSN号:1672-6421

关键字:semi-solid slurry; AZ91 magnesium; electromagnetic stirring; microstructure; near-liquidus

摘要:An electromagnetic stirring process near liquidus temperature was designed and demonstrated experimentally to produce semi-solid slurry of AZ91 magnesium alloy, in order to avoid not only contamination from mechanical stirring but also the inflammation of Mg alloy melt at elevated temperature. AZ91 alloy feedstock was isothermally heat treated at 600-610 degrees C for 20 min, and then stirred by electromagnetic field. Globular primary particle characteristic was observed optically in the castings. Mechanical properties were also studied.