发表刊物：COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS

收录刊物：SCIE、Scopus

卷号：562

页面范围：93-100

ISSN号：0927-7757

关键字：MnSiO3; Amorphous materials; Graphene oxide (GO); Composites; Supercapacitor; Electrochemical property

摘要：Manganese silicate/graphene oxide (MnSiO3/GO) composite was successfully synthesized using GO, manganese chloride and sodium silicate through a facile precipitation method. The results show MnSiO3 nanoparticles are closely dispersed on GO sheets, suggesting the formation of a united composite. This composite exhibits a large specific surface area of 161 m(2) g(-1) and a pore volume of 0.8728 cm(3) g(-1). MnSiO3/GO composite displays high electrical conductivity and fast ion and electron transport, which can improve the electrochemical performance of MnSiO3. To be specific, MnSiO3/GO composite delivers the specific capacitance as high as 262.5 F g(-1) at 0.5 A g(-1) in 1 M Na2SO4 electrolyte, which is higher than that of MnSiO3 (168.8 F g(-1)) and GO (4.6 F g(-1)). This finding proves that MnSiO3/GO composite can be considered as a promising candidate material applied to high-performance energy storage device.