Synthesis of V2O3/C composites with different morphologies by a facile route and phase transition properties of the compounds

点击次数:

论文类型:期刊论文

发表时间:2014-06-01

发表刊物:MATERIALS SCIENCE-POLAND

收录刊物:SCIE、EI

卷号:32

期号:2

页面范围:236-242

关键字:nanostructures; V2O3 amorphous carbon composites; chemical synthesis; phase transitions

摘要:V2O3 and amorphous carbon composites (V2O3/C composites) with different morphologies (e.g. nanospheres, nanorods and nanosheets) were, for the first time, successfully synthesized by a facile hydrothermal route and subsequent calcination. The as-obtained samples were characterized by X-ray powder diffraction (XRD), energy dispersive spectrometery (EDS), elemental analysis (EA), Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The morphology of V2O3/C composites could be easily controlled by varying the reaction time, and, as a result, V2O3/C composites with nanospheres, nanorods and nanosheets were selectively synthesized. Furthermore, the phase transition property of V2O3/C composites was measured by differential scanning calorimetry (DSC), suggesting that V2O3/C composites exhibit the phase transition similar to V2O3, which could expand the potential applications of materials related to V2O3 in the future.