Effect of GMA Polymer Compatibilizers on Highly Filled Composites of Low Density Polyethylene/Magnesium Hydroxide

点击次数:

论文类型:期刊论文

发表时间:2014-03-01

发表刊物:CHINESE JOURNAL OF POLYMER SCIENCE

收录刊物:SCIE、ISTIC、CSCD、Scopus

卷号:32

期号:3

页面范围:315-320

ISSN号:0256-7679

关键字:GMA; Grafted polymer; co-polymer; Polyethylene; Magnesium hydroxide

摘要:Functional polymers such as polyethylene grafted glycidyl methacrylate (PE-g-GMA) and ethylene-methyl acrylate-glycidyl methacrylate terpolymer (E/MA/GMA) were used as compatibilizers in the preparation of highly filled composites of polyethylene/magnesium hydroxide(PE/MH). Comparative studies were performed on the effect of magnesium hydroxide and stearic acid on the interface within polymer and magnesium hydroxide composites. The effect of polymeric compatibilizers on the properties of the composites was studied using tensile and impact tests, torque rheological analysis, differential scanning calorimetry and environmental scanning electron microscopy (ESEM). The microstructure of highly filled PE/MH composites changed after the addition of functional polymers. The mechanical properties of the composite material increased after compatibilization. The compatibilization processes of PE-g-GMA and E/MA/GMA were different. The grafted polymer was more compatible with polyethylene, which led to a polar polymer phase. In contrast, the tercopolymer tended to adhere to the surface of MH particles.