发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

收录刊物：SCIE、EI、Scopus

卷号：646

页面范围：279-287

ISSN号：0921-5093

关键字：Titanium alloy; Pre-strain; Mechanical twinning; Brittle omega phase; Ductility

摘要：This paper provided a novel approach for improving the strength-ductility tradeoff in beta titanium alloy through a combination of mechanical {332} < 113 > twins with brittle isothermal omega phase. Effects of pre-strain induced twins and subsequent precipitated omega phase on deformation microstructures, and tensile properties were investigated in a beta-type Ti-15Mo alloy (mass%). Mechanical twins increased with increasing pre-strain from 1% to 9%, while formation of isothermal omega phase at 523-673 K for 3.6 ks was not significantly affected by the pre-strain induced twins. Yield strength and uniform elongation characteristics depended strongly on degree of pre-strain and aging temperature. An effective combination of 1-4% pre-strain and subsequent aging at 523-573 K markedly enhanced the uniform elongation in range of 8-15% at the yield strength level of 800-1000 MPa. The enhanced uniform elongation was mainly attributable to further twinning activation during deformation in conjunction with pre-strain induced twins. (C) 2015 Elsevier B.V. All rights reserved.