发表刊物：CONSTRUCTION AND BUILDING MATERIALS

收录刊物：Scopus、EI、SCIE

卷号：148

页面范围：104-112

ISSN号：0950-0618

关键字：Reactive powder concrete; SiO2-coated TiO2; Mechanical behavior; Microstructural analysis

摘要：Nano SiO2-coated TiO2 (NSCT) is used to reinforce reactive powder concrete (RPC). The reinforcing mechanisms of NSCT are investigated through thermogravimetry (TG) analysis, X-ray powder diffraction (XRD) analysis, elemental analysis and scanning electron microscope (SEM) observation. The mechanical strengths of the NSCT reinforced RPC (NSCTRRPC) at different curing ages manifest significant increases, especially flexural behaviors. The flexural and compressive strengths of NSCTRRPC at age of 28 d achieve increases of 87%/6.69 MPa and 12.26%/12.2 MPa with respect to RPC without NSCT, respectively. TG analyses suggest that acceleration of cement hydration caused by nucleus effect plays a dominant role in the early days. XRD analyses manifests the NSCT decreases the amount of CH crystals in matrix. This suggests that the NSCT has the pozzolanic effect. In addition, element analysis is indicative that NSCT is uniformly distributed inside the matrix to make the cement matrix more compact, which is in consistent with SEM observations. It is therefore concluded that coating of nano SiO2 at the surface of TiO2 is beneficial for the dispersion of nano fillers in matrix and the pozzolanic effect, thus modifying the microstructures and the mechanical property of RPC. (C) 2017 Elsevier Ltd. All rights reserved.