点击次数：
论文类型：期刊论文
发表时间：2019-05-10
发表刊物：JOURNAL OF APPLIED POLYMER SCIENCE
收录刊物：SCIE、Scopus
卷号：136
期号：18
ISSN号：0021-8995
关键字：mechanical properties; resins; thermal properties; thermosets
摘要：A series of bismaleimide-triazine (BT) resins with and without O, O '-diallyl bisphenol A (DABPA) were produced by mixing 2, 2-bis (4-cyanatophenyl) propane (BADCy) and MCBMI (2,6-bis(4-(1-(4-(4-(2,5-dioxo-2,5-dihydro-1H-pyrrol-1-yl)phenoxy)-3-methylphenyl)-3-oxo-1,3-dihydroisobenzofuran-1-yl)-2-methylphenoxy)benzonitrile). The resins show just one glass-transition temperature (T-g) and enhanced flexural properties as well as superior fracture toughness compared with commercial BDM/BADCy system, in which BDM is (N,N '-bismaleimido-4,4 '-diphenylmethane). Introduction of DABPA can decrease the curing temperature of bismaleimide-triazine (BT) resins but increase its impact strength. When the mole of DABPA reach up to 1.2, the impact strength was increased by 1.34 times in comparison with BDM/ BADCy system. (c) 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 136, 47420.