原位生成二氧化钛对静电纺聚偏氟乙烯锂离子电池隔膜力学性能及电化学性能的影响

点击次数:
发表时间:2022-10-10
发表刊物:高分子学报
期号:11
页面范围:1319-1325
ISSN号:1000-3304
摘要:Composite nanofiber separators of polyvinylidene fluoride (PVDF) and titanium dioxide (TiO2) were prepared by electrospinning of PVDF solution containing in situ generated TiO2. The effects of TiO2 contents on the seperators' structure and properties were investigated. The morphology of seperators was characterized by scanning electron microscopy (SEM),and the fiber diameter distribution was also calculated using scnimage software. Differential scanning calorimetry (DSC) measurements were carried out to investigate seperator's thermal properties such as melting point, melting enthalpy and crystallinity. The mechanical strength was determined by tensile tests. The ionic conductivity was determined by AC impedence method, and the decomposition potential was determined by linear sweeping voltammetry (LSV). The results indicate that the seperator's tensile strength and elongation at break were improved remarkably after the addition of TiO2, with the maximum increase rate of 228.6% and 244.8%, respectively. The presence of TiO2 reduced the crystallinity of the seperators, which is benificial to the transfer of lithium ions. The polymer electrolytes' electrochemical performance was also enhanced, and the ionic conductivity at room temperature increased from 3.9 mS/cm to 5.1 mS/cm.
备注:新增回溯数据

 

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学