发表刊物：THERMOCHIMICA ACTA
收录刊物：SCIE、EI
卷号：514
期号：1-2
页面范围：44-50
ISSN号：0040-6031
关键字：Bismaleimide; Phthalide cardo structure; Cure behavior; Kinetics; Thermal properties
摘要：A novel bismaleimide containing phthalide cardo structure (BMIP) was mixed with 2,2'-diallylbisphenol A (DABPA), and the cure behavior of the mixture was studied by Fourier transform infrared (FTIR) spectroscopy and differential scanning calorimetry (DSC). The FTIR results demonstrated the cure reaction below 200 degrees C progressed preferentially via alternating copolymerization of maleimide and allyl groups. The DSC thermogram of the prepolymer showed three different cure regimes in the temperature range of 100-350 degrees C and the 2nd exothermic peak was predominant. The kinetic parameters of the 2nd curing process were evaluated using various kinetic models: Kissinger and Ozawa-Flynn-Wall, and the apparent activation energies obtained from two methods were consistent with each other. Thermal properties of the cured network were characterized by thermogravimetric analysis (TGA) and dynamic mechanical analysis (DMA). Experimental results exhibited that the onset decomposition temperature (T-5%) was similar to 431 degrees C and char yield at 600 degrees C was similar to 39.1%. In addition, the glass-transition temperature (T-g) reached 274 degrees C based on the tan delta peak temperature. (c) 2010 Elsevier B.V. All rights reserved.