点击次数：
论文类型：期刊论文
发表时间：2010-11-05
发表刊物：JOURNAL OF APPLIED POLYMER SCIENCE
收录刊物：SCIE、EI、Scopus
卷号：118
期号：3
页面范围：1606-1614
ISSN号：0021-8995
关键字：interface; cold plasma treatment; atomic force microscopy (AFM); XPS; DMTA
摘要：In this work, effects of the interface modification on the carbon fiber-reinforced epoxy composites were studied. For this purpose, the surface of carbon fibers were modified by oxygen plasma treatment. The surface characteristics of carbon fibers were studied by X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), dynamic contact angle analysis (DCAA), and dynamic mechanical thermal analysis (DMTA), respectively. The interlaminar shear strength (ILSS) was also measured. XPS and AFM analyses indicated that the oxygen plasma treatment successfully increased some oxygen-containing functional groups concentration on the carbon fiber surfaces, the surface roughness of carbon fibers was enhanced by plasma etching and oxidative reactions. DCAA and DMTA analyses show that the surface energy of carbon fibers increased 44.9% after plasma treatment for 3 min and the interfacial bonding intensities A and alpha also reached minimum and maximum value respectively. The composites exhibited the highest value of ILSS after oxgen plasma treated for 3 min. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 118: 1606-1614, 2010