关键字：Zn-HA; MAO; microstructure; binding

摘要：In order to improve the osteoblast growth and bacteria resistance, Zn-containing hydroxyapatite (Zn-HA) and titanium oxide (TiO2) composite coatings were prepared to improve binding between coating and Ti substrate. TiO2 film was prepared on the surface of Ti by micro-arc oxidation (MAO) and Zn-HA coating was deposited on TiO2 using sol gel technique. Phase structure, composition and microstructure of the surface coatings were analyzed by X-ray diffraction (XRD) and Energy Dispersive Spectrometer (EDS), respectively. The adhesion strength between the coatings with different Zn content was measured by tensile testing. The results showed that there was no significant influence of Zn content on adhesion strength between coating and Ti substrate.