点击次数：

论文类型：期刊论文

发表时间：2018-04-01

发表刊物：APPLIED SURFACE SCIENCE

收录刊物：SCIE、EI

卷号：436

页面范围：865-872

ISSN号：0169-4332

关键字：Superhydrophobic coating; Wood; Electromagnetic shielding; Self-leaning

摘要：A layer of superhydrophobic coating having good electromagnetic shielding and self-cleaning performance was fabricated on a wood surface through an electroless copper plated process. The superhydrophobic property of the wood surface was measured by contact angle (CA) and roll-off angle (RA) measurements. The microstructure and chemical composition of the superhydrophobic coating were analyzed by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and X-ray diffraction (XRD). The analysis revealed that the microscale particles were uniformly distributed on the wood surface and the main component of the coating is metallic copper. The as-prepared Cu coatings on wood substrate exhibit a good superhydrophobicity with water contact angle about 160 degrees and rolling angle less than 5 degrees. (C) 2017 Elsevier B.V. All rights reserved.