点击次数：

论文类型：期刊论文

发表时间：2018-12-01

发表刊物：JOURNAL OF MATERIALS SCIENCE

收录刊物：SCIE、Scopus

卷号：53

期号：23

页面范围：16099-16109

ISSN号：0022-2461

关键字：Alumina; Aluminum oxide; Corrosion protection; Corrosion resistance; Freezing; Rain; Silicones; Sodium chloride, Comparative tests; Corrosive conditions; Extreme environment; Hierarchical porous structures; Multi-functional; Resistance properties; Simple approach; Slippery surfaces, Aluminum corrosion

摘要：Slippery liquid-infused porous surface (SLIPS) inspired by Nepenthes pitcher has attracted considerable attention owing to its great potential applications in icy or corrosive conditions. However, observing both anti-icing property and corrosion resistance of SLIPS has rarely reported before. In this paper, a simple approach was proposed to prepare SLIPS to protect metal from freezing rain and corrosion. The Al substrate was first electrochemically etched and anodized to construct hierarchical porous structures composed of AlOOH and Al2O3. After lowering the surface energy and infusing silicone oil, the SLIPS was obtained showing a water roll-off angle of 3 degrees, which could exclude almost all liquids at an inclining angle of 5 degrees. Comparative tests including freezing rain and corrosion in NaCl solution, were conducted on bare Al and prepared oil-infused slippery surface, demonstrating the excellent anti-icing and corrosion resistance properties of our SLIPS. Additionally, self-cleaning test was also successfully performed. So, this slippery Al surface with multiple outstanding properties would be useful for the anti-icing and corrosion resistance applications in extreme environment.