Material loading in inverse surface integrity problem solution of cemented carbide component manufacturing by surface modification
点击次数:
论文类型:会议论文
发表时间:2016-06-08
收录刊物:SCIE、EI、CPCI-S
卷号:45
页面范围:235-238
关键字:Surface integrity; Surface modification; High-intensity pulsed ion beam; Material loading; High performance manufacturing
摘要:The inverse surface integrity problem could be effectively solved if the generation of a desired surface integrity be quantitatively correlated to process parameters or process loads. Possibility of establishing such a correlation is studied by employing a surface modification technique of high-intensity pulsed ion beam with well controlled thermo-mechanical load to manufacture WC-Ni cemented carbide component with enhanced wear resistance. The multiple surface integrity parameters including phase, microstructure and composition in addition to surface microhardness should be taken into account for establishing the correlation between process loads and surface integrity, since the interactions between the surface integrity parameters determine the wear performance of surface modified cemented carbides. The different process parameters can be quantitatively distinguished by material loading, i.e. the temperature and/or stress field evolution in the surface layer of cemented carbide under the different thermo-mechanical loads, while the material loading can be further correlated to the resultant changes in surface integrity. In this way, identification of material loading enables establishing a process-independent correlation between process loads and surface integrity for solving the inverse surface integrity problem. (C) 2016 The Authors. Published by Elsevier B.V.