大连理工大学主页平台管理系统石勇--中文主页-- Synthesis and characterization of bimetallic Cu-Al-BTC MOFs as an efficient catalyst for selective catalysis reduction of NO with CO

石勇 ( 副教授 ) 赞
的个人主页 http://faculty.dlut.edu.cn/sys99/zh_CN/index.htm
副教授硕士生导师
任职 : Royal Society of Chemistry（RSC）会员，Journal of Physics and Chemistry of Solids;Journal of Alloys and Compounds;《环境科学与技术》,《化学反应工程与工艺》等杂志特约审稿人。

论文成果当前位置: 中文主页 >> 科学研究 >> 论文成果

Synthesis and characterization of bimetallic Cu-Al-BTC MOFs as an efficient catalyst for selective catalysis reduction of NO with CO

点击次数：
论文类型：期刊论文
发表时间：2021-01-10
发表刊物：FERROELECTRICS
卷号：565
期号：1,SI
页面范围：58-65
ISSN号：0015-0193
关键字：Environmental catalysts; bimetallic MOFs; Cu-Al-BTC; CO-SCR
摘要：Bimetallic Cu-Al-BTC MOFs with various Cu/Al ratios were successfully synthesized via a hydrothermal method and applied for CO-SCR. It is found that the catalytic efficiency increased significantly with Cu:Al ratio from 1:1 to 6:1. 6Cu1Al-BTC catalyst exhibits the highest catalytic activity, which achieves nearly 100% NO conversion in the temperature range from 325 degrees C to 400 degrees C. All bimetallic Cu-Al-BTC catalysts showed higher catalytic activity than pure Cu-BTC and Al-BTC materials. The feasibility of bimetallic Cu-Al-BTC MOFs as a novel deNO(x)catalyst was evaluated in this work.