点击次数：

论文类型：期刊论文

发表时间：2018-01-16

发表刊物：Journal of colloid and interface science

收录刊物：SCIE

卷号：516

页面范围：254-262

ISSN号：1095-7103

关键字：Mesoporous,MnO(2),NH(3)-SCR

摘要：Employing nanocasting method, mesoporous MnO2 catalysts with large specific surface area and regular pore structure were synthesized by using three different types of mesostructure silicas (KIT-6, SBA-15, MCM-41) as hard templates. The physical and chemical properties of the three different mesostructured manganese oxide materials were comparatively and systematically characterized by using XRD, FT-IR, N2 adsorption-desorption, TEM, NH3-TPD, H2-TPR, XPS. The NH3-SCR performance of the mesoporous MnO2 was also evaluated on SCR self-assembly device. It was discovered that the mesostructure of the template would influence the amount and the kind of acid site, the reduction ability and then influence the catalytic performance of the materials. Mesoporous MnO2 templated from KIT-6 exhibited better catalytic performance than other mesoporous MnO2, indicating that the mesostructure of the materials has significant influence on the NH3-SCR performance. The KIT-6 templated MnO2 could induce 100% NOx conservation ratio range from 75 °C to 275 °C and exhibit good resistance of SO2 and H2O. Copyright © 2018 Elsevier Inc. All rights reserved.