NiO hierarchical structure: template-engaged synthesis and adsorption property

点击次数:

论文类型:期刊论文

发表时间:2012-11-07

发表刊物:RSC ADVANCES

收录刊物:SCIE、EI、Scopus

卷号:2

期号:27

页面范围:10217-10221

ISSN号:2046-2069

摘要:NiO hierarchical structure was synthesized via a facile template-engaged solvothermal reaction of Mg-5(CO3)(4)(OH)(2)center dot 4H(2)O and Ni(NO3)(2)center dot 6H(2)O, followed by annealing Ni-base precursor at high temperature in air. The as-prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and N-2 adsorption-desorption. It has been demonstrated that the NiO hierarchical structure retains the morphology of the template, and possesses a high surface area (over 58 m(2) g-(1)). Moreover, the growth mechanism of Ni-base precursor has been proposed. The porous hierarchical NiO exhibited good adsorption for the removal of organic dye pollutants from water. Thus, the porous hierarchical NiO is expected to find promising applications in catalysis, energy storage and sensors.