关键字：Al-Si composites; TiB2; composites; semisolid processing

摘要：Employing a cooling slope technique to produce semisolid slurry, in-situ 3wt%TiB2 particulate reinforced Al-12Si alloy composites have been successfully fabricated by flux-assisted synthesis method. It has been shown that the minute TiB2 particles with size 200-500nm uniformly distribute in the spherical alpha-Al structure and at the boundary of the eutectic Si. Two groups of contrast experiments with and without flowing on the slope have been performed to investigate the influence of the semisolid processing on the microstructure of the composites. Results have shown that alpha-Al grain is rather spherical and with an average size of 47.4 mu m, which indicates semisolid processing can be a potential route to produce metal matrix composites with high strength and good ductility.