In situ study on growth behavior of Cu6Sn5 during solidification with an applied DC in RE-doped Sn-Cu solder alloys
点击次数：
论文类型：期刊论文
发表时间：2014-10-01
发表刊物：JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
收录刊物：SCIE、EI
卷号：25
期号：10
页面范围：4538-4546
ISSN号：0957-4522
摘要：The growth behavior of Cu6Sn5 intermetallic compounds in rare earth (RE)-doped Sn-Cu solder alloys with an applied direct current (DC) has been in situ investigated using synchrotron radiation imaging technology. The morphological evolutions of Cu6Sn5 with various shapes of I-like, Y-like and bird-like are directly observed. After doping RE, the number of I-like and bird-like Cu6Sn5 is decreased, but the number of Y-like Cu6Sn5 is increased. The morphologies of Cu6Sn5 are more uniform and the mean lengths of Cu6Sn5 of different shapes are reduced in RE-doped alloys compared with that in RE-free alloys, which is attributed to the adsorption effect of RE. The growth orientation of Y-like Cu6Sn5 is changed after La is doped. Additionally, with an applied DC, the nucleation rate of Cu6Sn5 is increased and the growth rate is markedly enhanced resulting in the refinement of Cu6Sn5. Furthermore, the mechanisms of refinement caused by RE and DC are specifically discussed.