Performance of TS-1-Coated Structured Packing Materials for Styrene Oxidation Reaction
点击次数:
论文类型:期刊论文
发表时间:2011-05-01
发表刊物:ACS CATALYSIS
收录刊物:Scopus、SCIE、EI
卷号:1
期号:5
页面范围:437-445
ISSN号:2155-5435
关键字:TS-1 packing rings; film; contact area; styrene oxidation
摘要:Titanium silicalite-1 (TS-1)-coated on stainless steel packing rings of complex geometries provided a large interfacial contact area for improving mass transport processes. Zeolite seeds were assembled using organic linker, and a thin uniform layer of TS-1 catalyst was deposited on the surface by hydrothermal regrowth. The chemical, structural, and catalytic properties of the TS-1 layer were examined. An order of magnitude higher styrene conversion rate was obtained from the TS-1-coated substrates compared with powder. The catalyst was sensitive to pretreatment, and heat treatment in nitrogen provided a 30% higher conversion rate than the air-calcined samples. The N(2)-pretreated catalyst displayed lower activity loss and better regenerability.