点击次数：

论文类型：期刊论文

发表时间：2007-09-01

发表刊物：JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION

收录刊物：SCIE、EI、ISTIC、Scopus

卷号：22

期号：3

页面范围：551-554

ISSN号：1000-2413

关键字：high performance concrete; MK; autogenous shrinkage

摘要：Calcine and mill kaolin were used under agreeable technological conditions to generate matakaolin (MK). The autogenous shrinkage performance of high performance concrete added with MK was researched. It is shown that MK has an effective inhibitory action to early autogenous shrinkage of cement concrete, and the inhibitory action increases with the increase of MK. The autogenous shrinkage values from 24 hours after placement to 56 days are all higher than those of the contrasted concrete, among which, the value of the concrete with 5% MK is the highest. But the total shrinkage values in 56 days are all less than those of the contrasted test pieces. The total contraction after 24 h of placement decreases as the increase of MK, moreover, it is greatly less than that of the contrasted ones.