Crystallization behavior of poly(epsilon-caprolactone)/Tio2 nanocomposites obtained by in situ polymerization
点击次数:
论文类型:期刊论文
发表时间:2012-05-01
发表刊物:POLYMER ENGINEERING AND SCIENCE
收录刊物:SCIE、EI、Scopus
卷号:52
期号:5
页面范围:1047-1057
ISSN号:0032-3888
摘要:Poly(?-caprolactone) (PCL)/titanium dioxide (TiO2) nanocomposites were prepared by in situ polymerization of ?-caprolactone in the presence of modified-TiO2 nanoparticles as initiators. The molecular weight of PCL matrix was dependent on the amount of the TiO2 fillers. The incorporation of TiO2 did not significantly affect the crystalline structure of PCL. Moreover, a tendency of the nanoparticles to form aggregates was observed, especially at higher fillers contents. The analysis of the crystallization process showed that the addition of TiO2 nanoparticles accelerated the crystallization rate of PCL, and the crystallization rates increased by increasing the filler content. The crystallization activation energy dependence on the filler content observed here is probably the consequence of the two competing factors. The tendency of activation energy obtained by nonisothermal crystallization is similar to that of isothermal crystallization. POLYM. ENG. SCI., 2012. (C) 2011 Society of Plastics Engineers