论文类型：期刊论文

发表时间：2016-09-30

发表刊物：JOURNAL OF POWER SOURCES

收录刊物：SCIE、EI、Scopus

卷号：327

页面范围：178-186

ISSN号：0378-7753

关键字：Electrochemical hydrogen pump (EHP); SPPESK membrane; Hydrogenation; Hydrogen separation; Electrochemistry

摘要：This work reports the novel work of coupling H-2/CO2 separation with biomass-derived butanone hydrogenation in non-fluorinated sulfonated poly (phthalazinone ether sulfone ketone) (SPPESK) electro-chemical hydrogen pump (EHP) reactor. Due to higher resistance to swelling, SPPESK-based EHP reactor exhibits more excellent reaction rate in elevated temperature (60 degrees C) and higher butanone concentration (2 M) as 270, 260 nmol cm(-2) s(-1), respectively, higher than 240, 200 nmol cm(-2) s(-1) of Nafion-based EHP reactors. Also, the SPPESK-based EHP reactor remains 90% of initial hydrogenation rate after 4 batches, better than that of Nafion-based EHP reactors, which is only 62%. The energy efficiency of EHP separator reaches 40% under H-2/CO2 mixture feed mode, and electricity of about 0.3 kWh is consumed per Nm(3) H-2 product, being superior to energy consumption compared with alternative processes like PSA and electrolysis of water. In addition, SPPESK-based EHP exhibits better hydrogenation stability due to lower CO2 permeation than Nafion. With increasing CO2 content in H-2 feed, hydrogenation rate almost keeps constant at around 210 nmol cm(-2) s(-1) in SPPESK-based EHP reactor while decreases fast to 50 nmol cm(-2) s(-1) in Nafion/PTFE-based EHP reactor. These results show integration of gas separation with hydrogenation reactor is feasible in SPPESK-based EHP reactor. (C) 2016 Elsevier B.V. All rights reserved.