CuO-In2O3 Core-Shell Nanowire Based Chemical Gas Sensors
发表时间：2019-03-09
点击次数：
- 论文类型：
- 期刊论文
- 第一作者：
- Li, Xiaoxin
- 通讯作者：
- Li, XG (reprint author), Dalian Univ Technol, Sch Elect Sci & Technol, Inst Sensing Technol, Key Lab Liaoning Integrated Circuits Technol, Dalian 116024, Peoples R China.
- 合写作者：
- Li, Xiaogan,Chen, Ning,Li, Xinye,Zhang, Jianwei,Yu, Jun,Wang, Jing,Tang, Zhenan
- 发表时间：
- 2014-01-01
- 发表刊物：
- JOURNAL OF NANOMATERIALS
- 收录刊物：
- SCIE、EI
- 文献类型：
- J
- 卷号：
- 2014
- ISSN号：
- 1687-4110
- 摘要：
- The CuO-In2O3 core-shell nanowire was fabricated by a two-step method. The CuO nanowire core (NWs) was firstly grown by the conventional thermal oxidation of Cu meshes at 500 degrees C for 5 hours. Then, the CuO nanowires were immersed into the suspension of amorphous indium hydroxide deposited from the In(AC)(3) solution by ammonia. The CuO nanowires coated with In(OH)(3) were subsequently heated at 600 degrees C to form the crystalline CuO-In2O3 core-shell structure, with In2O3 nanocrystals uniformly anchored on the CuO nanowires. The gas sensing properties of the formed CuO-In2O3 core-shell nanowires were investigated by various reducing gases such as hydrogen, carbon monoxide, and propane at elevated temperature. The sensors using the CuO-In2O3 nanowires show improved sensing performance to hydrogen and propane but a suppressed response to carbon monoxide, which could be attributed to the enhanced catalytic properties of CuO with the coated porous In2O3 shell and the p-n junction formed at the core-shell interface.