点击次数：
发布时间：2019-12-06
论文类型：期刊论文
发表时间：2019-12-07
发表刊物：DALTON TRANSACTIONS
收录刊物：SCIE、EI
卷号：48
期号：45
页面范围：16974-16985
ISSN号：1477-9226
摘要：Herein, we have studied the crystallization of zeolite omega by the solid-state transformation of TMA-magadiite at 100 degrees C for 12 h. The samples prepared at different times were subjected to XRD, SEM, IR, Raman and solid MAS NMR analyses to investigate the crystallization behaviors and changes in the medium-range structure during the synthesis process and a comprehensive mechanism was proposed. It has been demonstrated that the 5Rs and 6Rs in magadiite are partially retained in the system and participate in the growth of zeolite omega. The 4Rs were formed after heating for 4 h. The synthesis time of the zeolite omega using this method is shorter than that using the magadiite hydrothermal conversion method (about 72 h), because special composition building units, which have similarities to the structure of zeolite omega, were formed and adsorbed on the surface of the TMA-magadiite, and then provided a growth surface for the synthesis of targets. In addition, recycling the waste mother liquid produced in the preparation of the precursor was done to achieve the low cost and green synthesis. Finally, several factors influencing the reaction are discussed.