发表刊物：INTERNATIONAL JOURNAL OF HYDROGEN ENERGY

收录刊物：SCIE、EI、Scopus

卷号：43

期号：1

页面范围：301-310

ISSN号：0360-3199

关键字：Cation exchange membrane; PPO; Long side chain; Vanadium redox flow battery; Microphase separation

摘要：A novel long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide) (S-L-PPO) membrane was successfully prepared for VRFB applications. The long side chains were introduced onto the PPO backbones by a simple and controllable acylation with 4-fluorobenzoyl chloride and a subsequent condensation with sodium 4-hydroxybenzenesulfonate. The introduction of long side chains drives the formation of a good hydrophilic/hydrophobic micro-phase separation structure, which is evidenced by AFM. The S-L-PPO membrane with a degree of sulfonation (DS) of 51% showed an ultralow vanadium permeability (4.3 x 10(-9) cm(2) s(-1)) and a decent proton conductivity (44 mS cm(-1)). As a result, the energy efficiency of VRFB with S-LPPO-51% membrane was up to 81.8% that was higher than that with Nafion 212 (78.0%) at a current density of 120 mA cm(-2). In addition, the self-discharge duration of the cell with S-LPPO-51% membrane was 222 h that was nine times longer than that of Nafion 212 (23 h). All these indicate that the membrane prepared here is promising for the application in VRFB. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.