发表刊物：AIP ADVANCES

收录刊物：SCIE、EI、CPCI-S

卷号：8

期号：5

ISSN号：2158-3226

摘要：The effects of Cu alloying on the amorphous-forming ability (AFA) and magnetic properties of the P-free Fe81Co5B11C2Si1 amorphous alloy were investigated. Addition of <= 1.0 at.% Cu enhances the AFA of the base alloy without significant deterioration of the soft magnetic properties. The Fe80.5Co5B11C2Si1Cu0.5 alloy with the largest critical thickness for amorphous formation of similar to 35 mu m possesses a high saturation magnetization (B-s) of similar to 1.78 T, low coercivity of similar to 14.6 A/m, and good bending ductility upon annealing in a wide temperature range of 513-553 K with maintaining the amorphous state. The fabrication of the new high-Fe-content Fe-Co-B-C-Si-Cu amorphous alloys by minor doping of Cu gives a guideline to developing high Bs amorphous alloys with excellent AFA. (C) 2017 Author(s).